Factory 0Cr15Al5 Strip Iron Chromium Aluminium Resistance Alloy For Furnace Applications
application area
Our products are widely used in heat treatment equipment, auto parts, iron and steel manufacturing,
aluminum industry, metallurgical equipment, petrochemical equipment, glass machinery, ceramic machinery,
food machinery, pharmaceutical machinery, and power engineering industry.
Chemical Content, %
| Alloy material | Chemical composition % |
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | others |
| max(≤) |
| 1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | - | 3.5-4.5 | Rest | - |
| 0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | - | 4.5-5.3 | Rest | - |
| 0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Rest | - |
| 0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Rest | - |
| 0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Rest | - |
| 0Cr19Al3 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 18.0-21.0 | ≤0.60 | 3.0-4.2 | Rest | - |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Rest | Nb add0.5 |
| 0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.2 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Rest |
|
Main technical characteristics of FeCrAl Alloy:
| Brand Property | 1Cr13Al4 | 1Cr21Al4 | 0Cr21Al6 | 0Cr23Al5 | 0Cr25Al5 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Major chemical component% | Cr | 12.0-12.5 | 17.0-21.0 | 19.0-22.0 | 20.5-23.5 | 23.0-26.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 2.0-4.0 | 5.0-7.0 | 4.2-5.3 | 4.5-6.5 | 5.0-7.0 | 6.0-7.0 |
| Fe | Balance | Balance | Balance | Balance | Balance | Balance | Balance |
| Re | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate | Appropriate |
|
|
|
|
|
| Addition Nb:0.5 | Addition Mo:1.8-2.2 |
| Component max. use temperature | 950 | 1100 | 1250 | 1250 | 1250 | 1350 | 1400 |
| Melting Point | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1510 |
| Density g/cm3 | 7.40 | 7.35 | 7.16 | 7.25 | 7.10 | 7.10 | 7.10 |
| Resistivity μΩ·m,20 | 1.25±0.08 | 1.23±0.06 | 1.42±0.07 | 1.35±0.06 | 1.45±0.07 | 1.45±0.07 | 1.53±0.07 |
| Tensile Strength Mpa | 588-735 | 637-784 | 637-784 | 637-784 | 637-784 | 637-784 | 684-784 |
| Extension rate% | 16 | 12 | 12 |
| 12 | 12 | 10 |
| Repeated bending frequency |
|
| 5 | 5 | 5 | 5 | 5 |
| Fast lift h/ | - |
|
| 80/1300 | 80/1300 |
| 50/1350 |
| Specific Heat J/g. | 0.490 | 0.490 | 0.520 | 0.460 | 0.494 | 0.494 | 0.494 |
| Heat Conduction Coefficient KJ/M.h | 52.7 | 46.9 | 63.2 | 60.1 | 46.1 | 46.1 | 45.2 |
| Linear expansion coefficient aX10-6/ (20-1000) | 15.4 | 13.5 | 14.7 | 15.0 | 16.0 | 16.0 | 16.0 |
| Hardness HB | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Microstructure | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic | Ferritic |
| Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |